E309L16 Electrode Welding Rod for Heat Treated Dissimilar Joints

feature: Good performance: low spatter tendency.

describe: E309L-16 provides a weld deposit E309-16, but with a reduced carbon content (up to 0.04%) for improved resistance to intergranular . Type E309L-16 is for for stainless steel to itself or to carbon or low alloy steel. E309L-16 is more suitable than E309-16 for cladding of carbon or low alloy steels and heat treated dissimilar joints.

suggestion: -1.0mm and 1.2mm electrodes have strict requirements on the current of the welding machine and need to be adjusted slowly. It is not recommended for beginners and those who are new to welding to use thin plate welding, especially below 1mm. 1.0mm and 1.2mm electrodes are too thin for welding. It will rock back and forth. For customers with rich welding experience, if they want to weld a thin plate of about 0.5mm, they can choose a 1.4mm electrode. Please check the current range of the electrode current before , so as not to cause unnecessary trouble to both parties. - The electrode should be baked at 300-350℃ for 1 hour before welding. - Try to use DC power supply, the current should not be too large.

Specification: Standard: GB/T983 E308-16 A5.4 E308-16 Diameter 1.0mm Length 250mm Current 9-22A Diameter 1.2mm Length 250mm Current 13-32A Diameter 1.4mm Length 250mm Current 16-40A Diameter 1.6mm Length 250mm Current 18-50A Diameter 1.8mm Length 250mm Current 20-55A Diameter: 2.0mm Length 300mm Current: 30-55A Diameter: 2.5mm Length 300mm Current: 50-100A Diameter: 3.2mm Length 350mm Current: 70-130A Diameter: 4.0mm Length 350mm Current: 100-160A

Packing list: 10PCS* electrode

Fraction: 1. Due to manual measurement, please allow 1-3mm difference, thank you for your understanding! 2. Due to the differences between different monitors, please understand that the images may not reflect the actual color of the item.